ABSTRACT
Abstract This study evaluated the surface characteristics and bond strength of Y-TZP treated with Er:YAG laser at different focal distances. 120 Y-TZP blocks were divided into five groups (n=24), according to the surface treatment: no treatment (C-); sandblasting with silica-coated aluminum oxide particles (C+); and Er:YAG laser application at focal distances of 1mm (Er:YAG-1), 4mm (Er:YAG-4), and 7mm (Er:YAG-7). Surface characteristics were analyzed using Vickers microhardness, confocal laser microscope, scanning electron microscopy (SEM), and X-ray diffractometer (XRD). For the bond strength test, 100 Y-TZP blocks were subdivided into two subgroups (n=10), according to the resin cement used: with (MDP+) or without 10-methacryloyloxydecyl dihydrogen phosphate (MDP-). The Vickers microhardness and surface roughness were analyzed by one-way ANOVA and bond strength by two-way ANOVA and Tukey's test for both (α=0.05). Vickers microhardness differences were not observed between the groups (p>0.05); C+ showed higher surface roughness values. SEM images showed micromorphological differences between the groups. The XRD data detected tetragonal crystals for C- and, for the other groups, tetragonal and monoclinic peaks. For bond strength, no statistically difference significance were observed among the cements with or without MDP (p>0.05) but showed significant difference between the surface treatments (C+ > C- = Er:YAG1 > Er:YAG4 = Er:YAG7) (p<0.05). Suggested that the Er:YAG laser cannot replace conventional treatment with aluminum oxide particles and the presence of MDP in the resin cement had no influence on the bond strength.
Resumo Este estudo avaliou as características de superfície e resistência de união de Y-TZP tratado com laser de Er: YAG em diferentes distâncias focais. Cento e vinte blocos de Y-TZP foram divididos em cinco grupos (n=24), de acordo com a superfície de tratamento: sem tratamento (C-); asperização com partículas de óxido de alumínio revestidas por sílica (C +); e aplicação de laser Er: YAG a distâncias focais de 1 mm (Er: YAG-1), 4 mm (Er: YAG-4) e 7 mm (Er: YAG-7). As características de superfície foram analisadas por meio de microdureza Vickers, microscópio confocal a laser, microscopia eletrônica de varredura (MEV) e difratômetro de raios-X (DRX). Para o ensaio de resistência de união, cem blocos de Y-TZP foram subdivididos em 2 subgrupos (n=10) de acordo com o cimento resinoso utilizado (n=12): com 10-metacriloiloxidecil dihidrogenofosfato (MDP+) ou sem (MDP-). Microdureza Vickers e rugosidade de superfície foram analisadas por ANOVA a 1 fator e a resistência de união por ANOVA a 2 fatores e ambos seguidos de teste complementar de Tukey (α=0,05). Não foram observadas diferenças de microdureza Vickers entre os grupos; C+ apresentou maiores valores de rugosidade superficial. Imagens de MEV mostraram diferenças micromorfológicas entre os grupos. Os dados de DRX detectaram apenas cristais tetragonais para C- e, para os outros grupos, picos de zircônia nas fases tetragonal e monoclínica. Para a resistência de união, não foram observadas diferenças estatisticamente significante entre os cimentos com e sem MDP (p>0.05), mas foram observadas diferenças significativas entre os tratamentos de superfície (C+ > C- = Er:YAG1 > Er:YAG4 = Er:YAG7) (p<0.05). Sugere-se que o laser de Er: YAG não pode substituir o tratamento convencional com partículas de óxido de alumínio e a presença de MDP no cimento resinoso não influenciou na resistência de união.
ABSTRACT
The aim of this study was to evaluate the efficacy of a pouring technique for implant-supported prostheses impressions. A metallic matrix (control group) with two implants positioned at 90 and 65 degrees was fabricated. The matrix was submitted to the direct transfer impression technique. In group CP (conventional pouring - n=10), casts were obtained by the conventional pouring technique. In group EP (experimental pouring - n=10), the analogs were embraced with latex tubes before the first pouring and then submitted to a second pouring. Vertical misfit and implants/analogs inclinations were evaluated. Data were analyzed by analysis of variance and Tukey's test (p<.05). Results demonstrated significant difference (p<.05) between control and experimental groups for misfit measurement in perpendicular implant/analog and between control group and group EP in leaning implant/analog. Considering inclination, there were significant differences (p<.05) between control and experimental groups for leaning analogs. Independently of the pouring technique, perpendicular implants produced more accurate casts.
O objetivo do estudo foi avaliar a eficacia de uma tecnica de vazamento para moldagens de proteses sobre implante. Uma matriz metalica (grupo controle) contendo dois implantes posicionados a 90° e 65° de inclinacao foi confeccionada. A matriz foi submetida a tecnica de moldagem de transferencia direta. No grupo CP (vazamento convencional - n=10), os modelos foram obtidos atraves da tecnica de vazamento convencional. No grupo EP (vazamento experimental - n=10), os analogos dos implantes foram revestidos por tubos de latex anteriormente ao primeiro vazamento e, entao, submetidos a um segundo vazamento. A desadaptacao vertical e a inclinacao dos implantes/analogos foram avaliadas. Os dados foram submetidos a Analise de Variancia e teste de Tukey (p<.05). Os resultados demonstraram diferenca significante (p<.05) entre os grupos controle e experimentais para a mensuracao da desadaptacao no implante/analogo perpendicular e entre os grupos controle e EP em relacao ao implante/analogo inclinado. Considerando a inclinacao, houve diferencas (p<.05) entre os grupos controle e experimentais em relacao a implante /analogos inclinados. Independentemente da tecnica de vazamento, implantes perpendiculares geraram modelos mais precisos.